Organotin polymers—XVI. Synthesis of p-acryloyloxybenzoic acid and n-methacryloyloxytetrabromophthalimide and copolymerizations with tri-n-butyltin acrylate and methacrylate
European polymer journal • 1992
Publication Information
Authors
AA Mahmoud, AF Shaaban, MM Azab, NN Messiha
Keywords
Not Available
Journal
European polymer journal
Publisher
Not Available
Volume
28
Issue
Not Available
Pages
555-559
publication.type
International
Paper Link
Open Link
Supplementary Materials
Not Available
Abstract
p-Acryloyloxybenzoic acid (ABA) and N-methacryloyloxytetrabromophthalimide
(NMTP) were prepared. The monomer reactivity ratios for the copolymerization of tri-n-
butyltin acrylate (monomer-1) with ABA and NMTP have been found to be r 1,= 1.01, r 2=
0.40 and r 1,= 0.69, r 2= 0.90 respectively; those for tri-n-butyltin methacrylate (monomer-l)
with ABA and NMTP were r 1= 2.21, r 2= 0.87 and r 1= 0.85, r 2= 1.35 respectively.
Copolymerizations were carried out in solution at 70 using 1 mol% azobisisobutyronitrile ...
(NMTP) were prepared. The monomer reactivity ratios for the copolymerization of tri-n-
butyltin acrylate (monomer-1) with ABA and NMTP have been found to be r 1,= 1.01, r 2=
0.40 and r 1,= 0.69, r 2= 0.90 respectively; those for tri-n-butyltin methacrylate (monomer-l)
with ABA and NMTP were r 1= 2.21, r 2= 0.87 and r 1= 0.85, r 2= 1.35 respectively.
Copolymerizations were carried out in solution at 70 using 1 mol% azobisisobutyronitrile ...