Organotin polymers—XVI. Synthesis of p-acryloyloxybenzoic acid and n-methacryloyloxytetrabromophthalimide and copolymerizations with tri-n-butyltin acrylate and methacrylate
European polymer journal • 1992
معلومات البحث
المؤلفون
AA Mahmoud, AF Shaaban, MM Azab, NN Messiha
الكلمات المفتاحية
Not Available
المجلة العلمية
European polymer journal
الناشر
Not Available
المجلد
28
العدد
Not Available
الصفحات
555-559
publication.type
International
رابط البحث
Open Link
المواد المرفقة
Not Available
الملخص
p-Acryloyloxybenzoic acid (ABA) and N-methacryloyloxytetrabromophthalimide
(NMTP) were prepared. The monomer reactivity ratios for the copolymerization of tri-n-
butyltin acrylate (monomer-1) with ABA and NMTP have been found to be r 1,= 1.01, r 2=
0.40 and r 1,= 0.69, r 2= 0.90 respectively; those for tri-n-butyltin methacrylate (monomer-l)
with ABA and NMTP were r 1= 2.21, r 2= 0.87 and r 1= 0.85, r 2= 1.35 respectively.
Copolymerizations were carried out in solution at 70 using 1 mol% azobisisobutyronitrile ...
(NMTP) were prepared. The monomer reactivity ratios for the copolymerization of tri-n-
butyltin acrylate (monomer-1) with ABA and NMTP have been found to be r 1,= 1.01, r 2=
0.40 and r 1,= 0.69, r 2= 0.90 respectively; those for tri-n-butyltin methacrylate (monomer-l)
with ABA and NMTP were r 1= 2.21, r 2= 0.87 and r 1= 0.85, r 2= 1.35 respectively.
Copolymerizations were carried out in solution at 70 using 1 mol% azobisisobutyronitrile ...