Structural, AC conductivity, dielectric behavior and magnetic properties of Mg-substituted LiFe5O8 powders synthesized by sol–gel auto-combustion method
Journal of Materials Science: Materials in Electronics • 2015
Publication Information
Authors
MG El-Shaarawy, MM Rashad, NM Shash, MH Maklad, FA Afifi
Keywords
Not Available
Journal
Journal of Materials Science: Materials in Electronics
Publisher
springer
Volume
26
Issue
8
Pages
6040-6050
publication.type
International
Paper Link
Open Link
Supplementary Materials
Not Available
Abstract
bstract Magnesium-substituted lithium ferrite powders (Li 1− x Mg 2x Fe 5− x O 8 where x=
0.0–0.8) were prepared by sol–gel auto-combustion method. XRD profiles revealed that all
compositions were single cubic ferrite structure for the precursors annealed at 800 C for 2 h.
The crystallite size was found to decrease whereas the lattice parameter was increased with
increasing Mg 2+ ion content. The microstructure of the formed powders was Mg
concentration dependent. Increasing the Mg 2+ ion ratio was found to inhibit the grain ...
0.0–0.8) were prepared by sol–gel auto-combustion method. XRD profiles revealed that all
compositions were single cubic ferrite structure for the precursors annealed at 800 C for 2 h.
The crystallite size was found to decrease whereas the lattice parameter was increased with
increasing Mg 2+ ion content. The microstructure of the formed powders was Mg
concentration dependent. Increasing the Mg 2+ ion ratio was found to inhibit the grain ...