This study provides a hydrometallurgical method to recover copper, lead, tin and gold from useless
printed circuit boards. Metals in the board were leached with different mineral acids. Gold, if present, was
first recovered by filtering from the acid solution, washed and polished. Metal salts went into the acidic
leachant were separately recovered, washed and dried. These were thermally reduced using carbon to obtain reduced metals. The polymeric base material was found safe for feasible for reuse in the manufacture
of new printed circuit boards. Parameters affecting the recovery factor were studied. Results obtained
showed that nitric acid was more effective compared to sulfuric or hydrochloric acid. The extent of metals
dissolution increases with increase in acid molarity, stoichiometric ratio, temperature and time of leaching.
With sulfuric acid, copper dissolved in > 6 M solution at > 75°C whereas lead and tin did not. With nitric
acid, all metals dissolved on hot conditions whereby tin deposited upon cooling as basic oxide. Lead was
separated from copper as chloride. Copper was separated as solid sulfide. The recovered compounds were
reduced with hydrogen gas or by carbon at temperatures up to 1000°C. A separation factor of 98.4-96.2%
was achieved.