Comparison of the structural properties of isomorphously substituted Fe in mordenite zeolites prepared by different methods
Journal of Colloid and Interface Science 259 (2003) 331–337 • 2003
Publication Information
Authors
Mohamed Mokhtar
Keywords
Keywords: Iron–mordenites; Ion exchange; Acid leaching; XRD; Texturing; Mössbauer spectroscopy
Journal
Journal of Colloid and Interface Science 259 (2003) 331–337
Publisher
Elsevier
Volume
Not Available
Issue
Not Available
Pages
Not Available
publication.type
International
Paper Link
Not Available
Supplementary Materials
Not Available
Abstract
Abstract
Fe was introduced in mordenite zeolite by means of ion exchange either in solid or in liquid state. The iron loading (50–200 wt%), iron
precursor (FeSO4·7H2O and FeCl3), and mordenite starting material (NH4M, HM, and NaM) were varied during the exchange processes.
The Fe species were characterized by N2 adsorption measurements as well as by XRD and Mössbauer spectroscopies. The Fe–mordenite
samples prepared by liquid-state ion exchange attained remarkable Fe dispersion and surface areas higher than those of the parent. It was
found that Fe3+ ions, which substituted the framework Al and accordingly occupied tetrahedral sites, were decreased with Fe loadings with
concomitant increase in Fe3+-occupied octahedral sites. The latter sites disappeared at 20 K to provoke the superparamagnetic α-Fe2O3 in
different particles size. The acid leaching (0.1 M HCl, 333 K, 3 h) of the samples showed the disappearance of the most highly distorted
extra-framework Fe3+ species, providing an indication of their presence on the external surface. On the other hand, a hematite phase was
detected in the solid-state ion exchange of FeCl3 with either HM or NH4M at the loading of 100% Fe.More correlations between Mössbauer
data on one hand and XRD and texturing properties on the other hand were evaluated and discussed.
Fe was introduced in mordenite zeolite by means of ion exchange either in solid or in liquid state. The iron loading (50–200 wt%), iron
precursor (FeSO4·7H2O and FeCl3), and mordenite starting material (NH4M, HM, and NaM) were varied during the exchange processes.
The Fe species were characterized by N2 adsorption measurements as well as by XRD and Mössbauer spectroscopies. The Fe–mordenite
samples prepared by liquid-state ion exchange attained remarkable Fe dispersion and surface areas higher than those of the parent. It was
found that Fe3+ ions, which substituted the framework Al and accordingly occupied tetrahedral sites, were decreased with Fe loadings with
concomitant increase in Fe3+-occupied octahedral sites. The latter sites disappeared at 20 K to provoke the superparamagnetic α-Fe2O3 in
different particles size. The acid leaching (0.1 M HCl, 333 K, 3 h) of the samples showed the disappearance of the most highly distorted
extra-framework Fe3+ species, providing an indication of their presence on the external surface. On the other hand, a hematite phase was
detected in the solid-state ion exchange of FeCl3 with either HM or NH4M at the loading of 100% Fe.More correlations between Mössbauer
data on one hand and XRD and texturing properties on the other hand were evaluated and discussed.