Synthesis and spectral characterization of CoxMg1-xAl2O4 as new coloring agent of ceramic pigments, Spectrochimica Acta PartA,74, 665–672.
• 2009
معلومات البحث
المؤلفون
I.S. Ahmed,S. A. Shama, M. M. Moustafa, H.A. Dessouki and A.A. Ali
الكلمات المفتاحية
Not Available
المجلة العلمية
Not Available
الناشر
Not Available
المجلد
Not Available
العدد
Not Available
الصفحات
Not Available
publication.type
International
رابط البحث
Open Link
المواد المرفقة
Not Available
الملخص
New nano-blue ceramic pigments of CoxMg1−xAl2O4 (0≤x≤0.1) have been prepared by coprecipitate–
combustion as a hybrid method using urea as a fuel at 500 ◦C in open furnace in air
atmosphere. The structure of pigment is assigned based on TGA/DTA/DrTGA analyses, X-ray diffraction
(XRD) and transmission electron microscopy (TEM). Also, electronic spectra, infrared (IR) and diffuse
reflectance spectroscopy (DRS) using CIE L*a*b* parameter measurement techniques were used. The
results revealed that the nano-particle size of pigments were obtained in the range 30–38nm as well as
the varying colors and particle size as a result of different calcinations temperatures within the range of
500–1200 ◦C for 2 h.
combustion as a hybrid method using urea as a fuel at 500 ◦C in open furnace in air
atmosphere. The structure of pigment is assigned based on TGA/DTA/DrTGA analyses, X-ray diffraction
(XRD) and transmission electron microscopy (TEM). Also, electronic spectra, infrared (IR) and diffuse
reflectance spectroscopy (DRS) using CIE L*a*b* parameter measurement techniques were used. The
results revealed that the nano-particle size of pigments were obtained in the range 30–38nm as well as
the varying colors and particle size as a result of different calcinations temperatures within the range of
500–1200 ◦C for 2 h.