Optimization of the cooling slope casting parameters for producing AA7075 wrought aluminumalloy thixotropic feedstock
• 2022
معلومات البحث
المؤلفون
E.Y.El-Kady1, I.S.El-Mahallawi2, T.S.Mahmoud1*,A.Attia1, S.S.Mohammed1,A.Monir1
الكلمات المفتاحية
Cooling slope casting;
Wrought aluminum alloys;
Microstructure.
المجلة العلمية
Not Available
الناشر
Not Available
المجلد
Not Available
العدد
Not Available
الصفحات
Not Available
publication.type
Local
رابط البحث
Not Available
المواد المرفقة
Amr Monier Abd Elaleem Ibraheem_optimization of the cooling slope casting parameters for producing AA7075 thixotropic feedstock.pdf
الملخص
Thixoforming technology requires a feedstock with a globular microstructure
rather than dendritic microstructure used in conventional casting
methods. In the present investigation, several AA7075 wrought aluminum
alloy feedstock were produced using cooling slope (CS) casting technique
at different fabrication conditions. Optimization of the CS castingprocess
parameterswas conductedto find out the optimum conditionsthat achieve
the best microstructural characteristics of the feedstock. Moreover, correlations
for microstructural characteristics as functions of CS casting
process parameters were determined. The results revealed that the optimum
values of pouring temperature, cooling length and tilt angle were
found to be 650 °C, 350 mm and 45°, respectively. Billets fabricated under
such conditions showed the minimum average size as well as the maximum
shape factor of á-Al primary grains. The pouring temperature is the
most influential parameter on both the average grain size and shape factor
of the primary á-Al grains.The developed empirical correlations were successfully
used to predict the average grain size and shape factor of the
AA7075 alloy billets produced using CS casting technique.
rather than dendritic microstructure used in conventional casting
methods. In the present investigation, several AA7075 wrought aluminum
alloy feedstock were produced using cooling slope (CS) casting technique
at different fabrication conditions. Optimization of the CS castingprocess
parameterswas conductedto find out the optimum conditionsthat achieve
the best microstructural characteristics of the feedstock. Moreover, correlations
for microstructural characteristics as functions of CS casting
process parameters were determined. The results revealed that the optimum
values of pouring temperature, cooling length and tilt angle were
found to be 650 °C, 350 mm and 45°, respectively. Billets fabricated under
such conditions showed the minimum average size as well as the maximum
shape factor of á-Al primary grains. The pouring temperature is the
most influential parameter on both the average grain size and shape factor
of the primary á-Al grains.The developed empirical correlations were successfully
used to predict the average grain size and shape factor of the
AA7075 alloy billets produced using CS casting technique.